ATLAS STOPTER K-20

2 in 1: adhesive for EPS and XPS application and for mesh embedding

 

100% Secure

 

Next Day Delivery Available

 

Return or change products

Description

Description 2 in 1 – designed for fixing thermal insulation boards and for the reinforced layer (base coat) installation in the external thermal insulation of buildings.
Element of the thermal insulation systems – an element of composite thermal insulation systems, granted the domestic (AT) and European (ETA) technical approvals.
Enables work in broad temperature range – not less than 0°C during works and not less than -5°C for 8 hours after completion.
The main characteristics• very high adhesiveness
• good water vapour permeability
• reinforced with microfibres
• resistant to cracks and scratches
• application in low temperatures (even from 0°C)
The main parameters• base coat bed thickness: 2 - 5 mm
• adhesion to expanded polystyrene: min. 0.1 MPa
• adhesion to concrete: min. 0.6 MPa
• consumption: boards application: from 4.0 to 5.0 kg/m²
• consumption: base coat application: from 3.0 to 3.5 kg/m²
USE

2 in 1 – designed for fixing thermal insulation boards and for the reinforced layer (base coat) installation in the external thermal insulation of buildings.

Element of the thermal insulation systems – an element of composite thermal insulation systems, granted the domestic (AT) and European (ETA) technical approvals.

Recommended for thermal insulation of passive and energy saving buildings – it helps obtaining the partition tightness required in passive building and also permanently fixes thermal insulation panels even 25 cm thick.

Enables fixing various expanded and extruded polystyrene boards – including graphite - enhanced, with addition of graphite and elasticized expanded polystyrene boards..

Enables work in broad temperature range – not less than 0°C during works and not less than -5°C for 8 hours after completion.

Increased resistance to cracking – it is reinforced with cellulose fibres.

High flexibility – perfectly compensates thermal and mechanical stress exerted on other layers of the system.

High adhesion – strongly bonds to problematic substrates, such as surfaces with well-bonded paint coats.

Water vapour permeability – does not restrict water vapour transmission through the insulated wall.

Data sheet

Data sheet
Model
K-20
Usage/Coverage
• consumption: boards application: from 4.0 to 5.0 kg/sqm
• consumption: base coat application: from 3.0 to 3.5 kg/sqm
Size
25 kg
Unit
bag